Putty powder for interior wall: mainly used for leveling the surface of base material, generally not directly applied to the paint surface. During the construction, the whole batch shall be scraped 2-3 times, the first batch shall be repaired mainly, and the second batch shall be scraped flat without exposing the bottom. 2m aluminum alloy ruler can be scraped horizontally and then longitudinally to meet the requirements of straightness and verticality. After drying, polish the wall and remove the polishing dust. The dosage is about 2.5-4.0kg/m2. Putty powder for inner wall with smooth surface: it should be used together with leveling putty powder for inner wall to meet the requirements of smooth and delicate basic surface.

　　腻子粉的施工方法通常是分批涂(刮)涂，由于需要用量大，施工劳动强度也大，所以一定要有好的施工质量，否则会直接影响腻子的使用。腻子粉的施工性能包括批刮和抛光。批刮是指腻子批刮手感柔软、光滑、无粘稠感，刮板批背无卷边，有适当的干燥时间，以便于对刮伤部位的缺陷进行适当的修改;良好的研磨性能是指腻子容易研磨光滑，研磨时不费力。

　　The construction method of putty powder is usually batch coating (scraping). Due to the large demand and the high labor intensity, it is necessary to have good construction quality, otherwise it will directly affect the use of putty. The construction performance of putty powder includes scraping and polishing. Scraping refers to the soft, smooth and non sticky feeling of putty scraping, no curling on the back of scraper scraping, and proper drying time, so as to facilitate the proper modification of the defects of the scraping parts; good grinding performance refers to the putty is easy to grind smooth and easy to grind.

　　平墙式内墙在腻子粉施工时一般批量刮2次，每次厚度不超过0.5mm。干燥后，打磨墙面，清除抛光灰尘。用量约为1.2-1.5kg/m2。平面内墙腻子粉:适用于普通场合，以满足涂料装饰工程对底面的一般要求。施工一般批量刮2次，每次厚度约1mm。干燥后，打磨墙面，清除抛光灰尘。用量约1.5-1.8kg/m2。注:一般抛光时间不宜过晚，约12-24小时为宜，过晚会影响抛光。

　　During the construction of putty powder, the flat wall type interior wall is generally scraped twice in batch, with the thickness not exceeding 0.5mm each time. After drying, polish the wall and remove the polishing dust. The dosage is about 1.2-1.5kg/m2. Putty powder for plane interior wall: it is suitable for ordinary occasions to meet the general requirements for the bottom surface of paint decoration engineering. Generally, the construction shall be scraped twice in batches, with a thickness of about 1mm each time. After drying, polish the wall and remove the polishing dust. The dosage is about 1.5-1.8kg/m2. Note: the general polishing time should not be too late, about 12-24 hours is appropriate, too late affects polishing.

　　有人认为光泽性和腻子粉的理化性质是一对矛盾,即腻子硬度高、物理化学性质是好的,是不容易的光泽,和光泽容易的腻子硬度差,物理化学性质性相对较低。这有一定道理，但不是全部。有些腻子可用于干燥后的腻子膜强度的时间差进行抛光。也就是说，腻子薄膜表面已干燥，可在腻子强度(硬度)时进行抛光，研磨时可提高极高。腻子粉易磨，但理化性能很好。

　　Some people think that the luster and the physical and chemical properties of putty powder are a pair of contradictions, that is, the hardness of putty is high, the physical and chemical properties are good, and the luster is not easy, and the hardness of putty with easy luster is poor, and the physical and chemical properties are relatively low. That makes sense, but not all. Some putty can be used for polishing the time difference of putty film strength after drying. That is to say, the surface of putty film is dry, and it can be polished when the strength (hardness) of putty is high, and it can be improved when grinding. Putty powder is easy to grind, but its physical and chemical properties are very good.

　　以上是济南腻子粉厂家为大家介绍的相关内容，想要了解更多内容，欢迎访问网站：https://www.jnfhjc.com

　　The above is the relevant content introduced by Jinan putty powder manufacturer. To learn more, please visit the website: https://www.jnfhjc.com